Quercetin reduces erosive dentin wear: Evidence from laboratory and clinical studies
Neng-Wu Jiang1, Deng-Wei Hong2, Thomas Attin3
1Fujian Key Laboratory of Oral Diseases & Fujian Provincial Engineering Research Center of Oral Biomaterial & Stomatological Key Laboratory of Fujian College and University, School and Hospital of Stomatology, Fujian Medical University, Fuzhou 350002, China; Department of Stomatology, Xiamen Branch, Zhongshan Hospital, Fudan University, Xiamen 361006, China.
Objective:
The aim of the present study was to evaluate the effect of quercetin on the acid resistance of human dentin through both laboratory and clinical studies.
Methods:
Two hundred and twelve dentin blocks (2 mm × 2 mm × 2 mm) were prepared and used. For the laboratory study, dentin specimens were randomly divided into 8 groups (n = 12): deionized water, ethanol, 1.23 × 104 μg/ml sodium fluoride (NaF), 120 μg/ml chlorhexidine, 183.2 μg/ml epigallocatechin gallate (EGCG), and 75 μg/ml, 150 μg/ml, and 300 μg/ml quercetin (Q75, Q150, and Q300). The specimens were treated with the respective solutions for 2 min and then subjected to in vitro erosion (4 cycles/d for 7 d). The surface microhardness loss (%SMHl), erosive dentin wear, and surface morphology were evaluated and compared. For the impact on MMP inhibition, the release of crosslinked carboxyterminal telopeptide of type I collagen (ICTP) and the thickness of the demineralized organic matrix (DOM) were measured using additional dentin specimens. For the clinical study, the specimens were treated with NaF or Q300 for 2 min and then subjected to in vivo erosion (4 cycles/d for 7 d). The %SMHl and erosive dentin wear of the specimens were measured to determine whether quercetin similarly inhibits erosion in situ.
Results:
The quercetin-treated group had a significantly lower %SMHl and erosive dentin wear than any other group, and the effect was concentration-dependent in vitro (P < 0.05). Dentin treated with quercetin produced significantly less ICTP and had a thicker DOM than the control dentin (P < 0.05). After in vivo erosion, the %SMHl and erosive dentin wear of the Q300 group were significantly lower than those of the control group (P < 0.05).
Significance:
The application of quercetin was shown, for the first time, to increase the acid resistance of human dentin, possibly through MMP inhibition and DOM preservation.