Construction and Transition Metal Oxide Loading of Hierarchically Porous Carbon Aerogels

Hierarchically porous carbon aerogels (CAs) were prepared by organic condensation gelation method combined with atmospheric drying and pore-formation technology, followed by a carbonization process. With as-prepared CAs as substrate, the transition metal oxide nanoparticles loaded CAs composites (MnO₂/Mn₂O₃@CA and Ni/NiO@CA) were achieved by means of liquid etching method combined with heat treatment, respectively. The catalyst, pore-forming agent and etching have important roles on the apparent density and pore structure of CAs. The hydrochloric acid (catalyst) significantly accelerates the gelation process and influences the size and distribution of macropores, whereas the addition of PEG2000 (pore-forming agent) and the etching of liquid solution leads to the formation of mesopore structure in CAs. Appropriate amounts of hydrochloric acid and PEG2000 allow the formation of hierarchically porous CAs with a BET surface area of 482.9 m²·g^-1 and a macropore size of 11.3 μm. After etching and loading, the framework of CAs is etched to become a mesoporous structure, and the transition metal oxide nanoparticles can be uniformly loaded in CAs. These resultant composites have promising application in super capacitor, electrocatalysis, batteries and other fields.