Related Experiment Video

Updated: Dec 8, 2025

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

626

Fracture resistance, failure mode and stress concentration in a modified endocrown design

Wiam El Ghoul1, Mutlu Özcan2, Joao Paulo Mendes Tribst3

  • 1Department of Prosthodontics, Faculty of Dental Medicine, Lebanese University, Beirut, Lebanon.

Biomaterial Investigations in Dentistry
|September 17, 2020
PubMed
Abstract

Keywords:
Endocrownfailure modefinite element analysisfracture resistancelithium disilicate

More Related Videos

Fracture Apparatus Design and Protocol Optimization for Closed-stabilized Fractures in Rodents06:59

Fracture Apparatus Design and Protocol Optimization for Closed-stabilized Fractures in Rodents

Published on: August 14, 2018

13.9K
An Improved Mechanical Testing Method to Assess Bone-implant Anchorage11:51

An Improved Mechanical Testing Method to Assess Bone-implant Anchorage

Published on: February 10, 2014

15.8K

Related Concept Videos

Stress Concentrations01:24

Stress Concentrations

Stress concentration is when stress intensifies near discontinuities such as holes or abrupt cross-sectional changes in a structural member. This localized stress can often surpass the average stress within the member. The stress distribution in flat bars, either with a circular hole or varying widths connected by fillets, can be determined experimentally using a photoelastic method. The results are based on ratios of geometric parameters like the ratio of the hole's radius to the smaller...
526
Stress Concentrations01:13

Stress Concentrations

The concept of stress concentration is crucial for understanding how materials respond under bending stresses, particularly when there are irregularities or discontinuities in the material's geometry. Normally, stress in a symmetric member subjected to pure bending is assumed to be uniformly distributed across the entire cross-section. However, this assumption does not hold when there are variations in the cross-sectional geometry or the presence of notches and holes.
The stress...
477
Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
667
Stress-Strain Diagram - Brittle Materials01:24

Stress-Strain Diagram - Brittle Materials

Brittle materials, including glass, cast iron, and stone, exhibit unique characteristics. They fracture without considerable change in their elongation rate, indicating that their breaking and ultimate strength are equivalent. Such materials also show lower strain levels at the point of rupture. The failure in brittle materials predominantly results from normal stresses, as evidenced by the rupture created along a surface perpendicular to the applied load. These materials do not display...
3.4K
Behavior of Concrete Under Compressive Load01:23

Behavior of Concrete Under Compressive Load

Concrete exhibits specific behaviors under different compressive loads. Understanding this is crucial for understanding its structural integrity. When concrete undergoes uniaxial compression, it tends to develop cracks that run parallel to the direction of the force. These parallel cracks stem from localized tensile stresses that occur perpendicular to the compression direction. Additionally, angled cracks may appear due to the formation of shear planes.
As the concrete specimen fractures under...
448
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
324