Simple Method for Efficient Slot-Die Coating of MAPbI₃ Perovskite Thin Films in Ambient Air Conditions

Scalable methods for deposition of lead halide perovskite thin films are required to enable commercialization of the highly promising perovskite photovoltaics. Here, we have developed a slot-die coating process under ambient conditions for methylammonium lead iodide (MAPbI₃) perovskite on heated substrates (about 90 °C on the substrate surface). Dense, highly crystalline perovskite films with large grains (100-200 μm) were obtained by careful adjustment of the deposition parameters, using solutions that are similar but more dilute than those used in typical spin-coating procedures. Without any further after treatments, such as antisolvent treatment or vapor annealing, we achieved power conversion efficiencies up of 14.5% for devices with the following structure: conducting tin oxide glass (FTO)/TiO₂/MAPbI₃/spiro-MeOTAD/Au. The performance was limited by the significant roughness of the deposited films, resulting from the hot-casting method, and the relatively high deposition temperature, which led to a defect-rich surface due to loss of MAI.