Changes in the Dimensions of Lignocellulose Nanofibrils with Different Lignin Contents by Enzymatic Hydrolysis

Changes in the dimensions of lignocellulose nanofibrils (LCNFs) with different lignin contents from betung bamboo (Dendrocalamus asper) by enzymatic hydrolysis using endoglucanase (EG) were investigated. Lignin contents were adjusted from 3% to 27% by NaClO₂/acetic acid treatment, and LCNFs were prepared using a wet disk-mill (WDM). The dimensions of the LCNFs significantly decreased with decreasing lignin content and increasing EG addition. With increasing EG content, the average diameter of the LCNFs significantly decreased, even though they contained parts of hemicellulose and lignin. The crystal structure showed the typical cellulose I structure in all samples, but the intensity of the diffraction peak slightly changed depending on the lignin and EG contents. The crystallinity index (CrI) values of the LCNFs increased a maximum of 23.8% (LCNF-L27) under increasing EG addition, regardless of the lignin content. With the EG addition of three times the LCNF amount, LCNF-L3 showed the highest CrI value (59.1%). By controlling the composition and structure of LCNFs, it is expected that the wide range of properties of these materials can extend the property range available for existing materials.