Glycerol Phosphate Dimethacrylate: An Alternative Functional Phosphate Ester Monomer to 10-Methacryloyloxydecyl
Fei Han1, Shiqi Dai1, Jiaxue Yang1
1Jiangsu Key Laboratory of Oral Diseases; Department of Prosthodontics, Affiliated Hospital of Stomatology, Nanjing Medical University, Nanjing 210029, China.
Abstract:
The bonding performance of a glycerol phosphate dimethacrylate (GPDM)-based, two-step, self-etch (SE) adhesive was experimentally compared to that of 10-methacryloyloxydecyl dihydrogen phosphate (MDP)-based universal adhesives in different application modes for enamel bonding. Microtensile bond strength (μTBS) for adhesives bonded to enamel was measured initially (24 h water storage) and after 10 000 thermocycles plus water storage for 30 days. A GPDM-based, two-bottle, two-step, self-etch adhesive (Optibond Versa, OV) and three one-bottle MDP-based universal adhesives, one self-etching (Tetric N Bond Universal, TNBU) and two with etch-and-rinse (E&R) processing (Single Bond Universal (SBU); Clearfil Universal Bond Quick (CUBQ)), were tested. Scanning electron microscopy (SEM) evaluated nanoleakage at the bonding interfaces. A profilometer determined roughnesses of enamel surfaces after phosphoric acid etching, OV priming, or TNBU conditioning. SEM observed the corresponding surface morphology. NMR and X-ray photoelectron spectroscopy (XPS) characterized chemical bonding in hydroxyapatites (HAps) conditioned with the adhesives. Etch-and-rinse samples had significantly stronger bonding than self-etch samples (p < 0.05) irrespective of aging. The μTBS values for initial and aged OV were significantly higher than those of TNBU (p < 0.05). Aging did not significantly decrease μTBS for any sample except TNBU (p < 0.05), but it significantly aggravated nanoleakage. Etch-and-rinse processing resulted in less nanoleakage than self-etching; the OV samples leaked less than TNBU, both before and after aging. Phosphoric acid etching achieved the highest enamel surface roughness, followed by OV primer. Ca-O-P bonds in hydroxyapatite conditioned with TNBU, SBU, and CUBQ were confirmed by NMR, which showed similar results to XPS observations of conditioned hydroxyapatite powders except OV primer. The GPDM-based, two-step, self-etch adhesive can provide higher micromechanical retention potential, bond strength, and durability than the MDP-based universal adhesive in self-etch mode but lower performance than the MDP-based universal adhesive in etch-and-rinse mode. None of the tested adhesives could avoid nanoleakage after aging.
More Related Videos
08:26Development of Amelogenin-chitosan Hydrogel for In Vitro Enamel Regrowth with a Dense Interface
Published on: July 10, 2014
15:33Microwave-assisted Functionalization of Polyethylene glycol and On-resin Peptides for Use in Chain Polymerizations and Hydrogel Formation
Published on: October 29, 2013
Related Concept Videos
01:01Phosphodiester Linkages
Phosphodiester bond forms when a phosphoric acid molecule (H3PO4) links with two hydroxyl groups (–OH) of two other molecules, forming two ester bonds. Two water molecules are released in this process. The phosphodiester bond is commonly found in nucleic acids (DNA and RNA) and plays a critical role in their structure and function.
Phosphodiester Bonds Link Nucleotides Together
DNA and RNA are polynucleotides or long chains of nucleotides that are linked together. A nucleotide is...
01:14Alkylation of β-Diester Enolates: Malonic Ester Synthesis
02:22Overview of Advanced Functional Groups
Functional groups are groups of atoms with specific chemical properties that occur within organic molecules and are sometimes denoted as “R”. Functional groups can “functionalize” a compound by enabling it to adopt different physical and chemical properties.
Types of Advanced Functional Groups
The table below summarizes some of the major functional groups in organic chemistry.
01:20Types of Step-Growth Polymers: Polyesters
Polyesters are commonly prepared from terephthalic acid and ethylene glycol; the crude product is known as poly(ethylene terephthalate) or PET. However, polyesters are synthesized industrially by transesterification of dimethyl terephthalate with ethylene glycol at 150 °C. The two reactants and the polymer...