Preparation of Poly-1-butene Nanofiber Mat and Its Application as Shutdown Layer of Next Generation Lithium Ion...

Nonwoven nanofiber webs from polyolefin show great potential in various fields such as nanofilters, high performance membranes and separators in lithium ion batteries (LiB). Although nonwoven microfiber webs can be obtained by the well-established melt-blown method, it is relatively difficult to produce nonwoven nanofiber web using polyolefin (polyethylene and polypropylene). There have been several reports on the preparation of polyolefin nanofibers by melt-electrospinning, although this approach presents several intrinsic disadvantages, i.e., high processing costs, the requirement of complex equipment, and poor control over pore size or fiber diameter. Solution-based electrospinning has the potential to overcome the drawbacks of melt-electrospinning, but the solubility of most polyolefin is poor. In this study, we found that poly-1-butene, a member of the poly(alpha-olefin) family, can be used in the electrospinning process. We set the concentration of the polymeric solution for electrospinning at 0.65-1.7 g/mL. Here, we report on the fabrication of nonwoven fiber webs composed of poly-1-butene and their copolymers. The diameter of the nonwoven fiber mat was 0.2-0.4 μm, which can be applicable for shutdown layer. As a representative application, we prepared a poly-1-butene nanofiber separator with an appropriate pore size by electrospinning for use as the shut-down layer of a next-generation LiB. The PB-based nanofiber mat provided shutdown ability at around 100 to 120 °C.