Effect of layer-distributed carbon nanotube (CNT) on mechanical and piezoresistive performance of intelligent...

Agglomerated carbon nanotube (CNT) powder was scattered into a cement paste layer-by-layer to form layer-distributed CNT composite (LDCC) as intelligent cement-based sensor. The characteristic of the CNT agglomerations and its effect on the mechanical and piezoresistive properties of cement paste were investigated in this study, and the results were compared with those of uniformly-dispersed CNT composites (UDCC). Based on the statistics of CNT agglomerations, it was found that the sizes of agglomerations varied from several to dozens of micrometres. The larger sized agglomerations with poorer roundness exhibited a higher possibility to cause the pores or voids accompanied with stress concentration when subjected to external forces. Hence, it is necessary to control the agglomeration sizes to reduce the porosity with edges and corners. The UDCC reached the highest compressive strength, followed by the plain cement paste and then LDCC. The mechanical strength of LDCC decreased with the increase of CNT layers. The piezoresistivity occurred in both the UDCC and LDCC, with the former possessing stable and repeatable performance. In addition, the strain-sensing ability of LDCC with moderate CNT layers presented similar sensing efficiency and repeatability to that of UDCC. The related results provide insight into the intelligent cement-based sensors with layer-distributed CNT and agglomerations, which can improve the efficiency and effectively reduce the cost for practical application.