Long-term antibacterial activity of a composite coating on titanium for dental implant application

Dental implants are the most innovative and superior treatment modality for tooth replacement. However, titanium implants still suffer from insufficient antibacterial capability and peri-implant diseases remain one of the most common and intractable complications. To prevent peri-implant diseases, a composite coating containing a new antibacterial agent, (Z-)-4-bromo-5-(bromomethylene)-2(5H)-furanone (BBF) was fabricated on titanium. This study was designed to investigate the antibacterial activity of the composite coating against two common peri-implant pathogens (Porphyromonas gingivalis and Actinobacillus actinomycetemcomitans). The morphology of the composite coating showed that BBF-loaded poly(L-lactic acid) nanospheres were well-distributed in the pores of the microarc oxidation coating, and cross-linked with each other and the wall pores by gelatin. A release study indicated that the antibacterial coating could sustain the release of BBF for 60 d, with a slight initial burst release occurring during the first 4 h. The antibacterial rate of the composite coating for adhering bacteria was the highest (over 97%) after 1 d and over 90% throughout a 30-day incubation period. The total fluorescence intensity of the composite coating was the lowest, and the vast majority of the fluorescence was red (dead bacteria). Moreover, real-time polymerase chain reaction analysis confirmed that the relative gene expression of the adherent bacteria on the composite coating was down-regulated. It was therefore concluded that the composite coating fabricated on titanium, which showed excellent and relatively long-term antibacterial activity against Porphyromonas gingivalis and Actinobacillus actinomycetemcomitans, is a potential and promising strategy to be applied on dental implants for the prevention of peri-implant diseases.