Color and masking properties of translucent monolithic zirconia before and after glazing

Purpose 1. to assess the ability of four brands of translucent monolithic zirconia with different thicknesses to mask discolored substrates; 2. to assess the influence of glazing upon their color coordinates and masking properties.Methods Sixty samples of shade A1 (0.8, 1.5, and 2.0 mm thickness) from: ZirCAD/MT, Katana/HT, Vita YZ/HT, Cercon/HT were fabricated and glazed using a standardized laboratory procedure. CIE L*a*b* parameters were recorded on composite substrates, (IPS Natural Die Material Kit) (ND1=reference; ND2, ND3, ND4, ND5=test backgrounds), before and after glazing. The color changes of zirconia samples induced by glazing were analyzed. Masking properties was calculated as the color difference between CIE L*a*b* parameters of the samples placed on reference and test substrates with CIEDE2000(1:1:1) formula. The effect of material, thickness, substrate, and glazing on the color of monolithic zirconia was analyzed with ANOVA test and the multiple comparisons were analyzed with Tukey HSD tests (α=0.05).Results After glazing, lightness L* significantly increased, while chromatic coordinates a* and b* decreased (p<0.05). Significant differences in the masking properties of the four materials (p<0.001) were found, with IPS e.max ZirCAD/MT having the lowest masking effect (p<0.001). Thickness, substrate and glazing had a significant effect on the color masking properties of monolithic zirconia (p<0.001).Conclusions Masking properties of translucent zirconia were significantly influenced by the materials, the thickness and the color of the substrate; moreover, glazing improved the masking ability for all zirconia samples.