The Role of Titanium Dioxide on the Hydration of Portland Cement: A Combined NMR and Ultrasonic Study

Titanium dioxide (TiO₂) is an excellent photocatalytic material that imparts biocidal, self-cleaning and smog-abating functionalities when added to cement-based materials. The presence of TiO₂ influences the hydration process of cement and the development of its internal structure. In this article, the hydration process and development of a pore network of cement pastes containing different ratios of TiO₂ were studied using two noninvasive techniques (ultrasonic and NMR). Ultrasonic results show that the addition of TiO₂ enhances the mechanical properties of cement paste during early-age hydration, while an opposite behavior is observed at later hydration stages. Calorimetry and NMR spin-lattice relaxation time T₁ results indicated an enhancement of the early hydration reaction. Two pore size distributions were identified to evolve separately from each other during hydration: small gel pores exhibiting short T₁ values and large capillary pores with long T₁ values. During early hydration times, TiO₂ is shown to accelerate the formation of cement gel and reduce capillary porosity. At late hydration times, TiO₂ appears to hamper hydration, presumably by hindering the transfer of water molecules to access unhydrated cement grains. The percolation thresholds were calculated from both NMR and ultrasonic data with a good agreement between both results.