Thermal, morphological, and spectral changes after Er, Cr:YSGG laser irradiation at low fluences on primary teeth for...

The aim of this study was to determine the temperature increase in the pulp chamber and possible thermal effects on molecular structure of primary teeth during the irradiation with Er,Cr:YSGG laser. Primary central incisors were divided into three groups (n = 20). Labial surfaces in each group were irradiated by Er,Cr:YSGG laser within different power and frequencies as following groups: I: 0.25 W, 20 Hz, II: 0.50 W, 20 Hz, III: 0.75 W, 20 Hz. A thermocouple was placed inside the pulp chamber so that the temperature increments were recorded during the enamel irradiation. Morphological changes of enamel surfaces were experimentally evaluated by SEM. Fourier-transform infrared spectroscopy and RAMAN analyses were carried out to determine the differentiations in the molecular structure. The experimental results obtained were analyzed statistically by means of one-way analysis of variance. Statistically significant differences were detected between groups (p < .05). Group III exhibited the highest values for the temperature parameters. Besides, the conical craters, cracks, and formation of ablation areas were observed for all the groups. Also, it was obtained that the hydroxyapatite lost the hydroxyl ions due to the thermal effect of the laser. Temperature rise throughout the Er,Cr:YSGG laser irradiation for prevention of primary enamel demineralization presented a positive correlation with the laser output power level. The formations of adverse morphological and spectral changes were detected on the surface of teeth after the laser application. On this basis, the Er,Cr:YSGG laser applications should be treated with much more caution considering enamel surface and pulpal tissues in primary teeth.