Influence of MXene (Ti₃C₂) Phase Addition on the Microstructure and Mechanical Properties of Silicon Nitride Ceramics

This paper discusses the influence of Ti₃C₂ (MXene) addition on silicon nitride and its impact on the microstructure and mechanical properties of the latter. Composites were prepared through powder processing and sintered using the spark plasma sintering (SPS) technic. Relative density, hardness and fracture toughness, were analyzed. The highest fracture toughness at 5.3 MPa·m^1/2 and the highest hardness at HV5 2217 were achieved for 0.7 and 2 wt.% Ti₃C₂, respectively. Moreover, the formation of the Si₂N₂O phase was observed as a result of both the MXene addition and the preservation of the α-Si₃N₄→β-Si₃N₄ phase transformation during the sintering process.