Unique Slow Crack Growth Behavior of Isotactic Polypropylene: The Role of Shear Layer-Spherulites Layer Alternated

Mingjin Liu1, Jiaxu Luo1, Jin Chen1

  • 1State Key Laboratory of Polymer Materials Engineering, College of Polymer Science and Engineering, Sichuan University, Chengdu 610065, China.

Polymers
|November 25, 2020
PubMed

Keywords:
alternated structureiPPslow crack growth

More Related Videos

Fabrication of a Bioactive, PCL-based "Self-fitting" Shape Memory Polymer Scaffold09:37

Fabrication of a Bioactive, PCL-based "Self-fitting" Shape Memory Polymer Scaffold

Published on: October 23, 2015

13.2K
Studying Large Amplitude Oscillatory Shear Response of Soft Materials06:07

Studying Large Amplitude Oscillatory Shear Response of Soft Materials

Published on: April 25, 2019

13.3K

Related Concept Videos

Polymer Classification: Stereospecificity01:26

Polymer Classification: Stereospecificity

Polymerization generates chiral centers along the entire backbone of a polymer chain. Accordingly, the stereochemistry of the substituent group has a significant effect on polymer properties. Polymers formed from monosubstituted alkene monomers feature chiral carbons at every alternate position in the polymer backbone. Relative to the predominant orientation of substituents at the adjacent chiral carbons, the polymer can exist in three different configurations: isotactic, syndiotactic, and...
3.0K
Anionic Chain-Growth Polymerization: Mechanism01:04

Anionic Chain-Growth Polymerization: Mechanism

The mechanism for anionic chain-growth polymerization involves initiation, propagation, and termination steps. In the initiation step, a nucleophilic anion, such as butyl lithium, initiates the polymerization process by attacking the π bond of the vinylic monomer. As a result, a carbanion, stabilized by the electron‐withdrawing group, is generated. The resulting carbanion acts as a Michael donor in the propagation step and attacks the second vinylic monomer, which acts as a Michael...
2.3K
Step-Growth Polymerization: Overview01:03

Step-Growth Polymerization: Overview

Step-growth or condensation polymerization is a stepwise reaction of bi or multifunctional monomers to form long-chain polymers. As all the monomers are reactive, most of the monomers are consumed at the early stages of the reaction to form small chains of reactive oligomers, which then combine to form long polymer chains in the late stages. Hence, the reaction has to proceed for a long time to achieve high molecular weight polymers.
Many natural and synthetic polymers are produced by...
4.1K
Anionic Chain-Growth Polymerization: Overview01:20

Anionic Chain-Growth Polymerization: Overview

The polymerization process that involves carbanion as an intermediate is called anionic polymerization. It is also a type of addition or chain-growth polymerization. Anionic polymerization gets initiated by a strong nucleophile such as an organolithium or a Grignard reagent. The most commonly used initiator for anionic polymerization is butyl lithium. Monomers involved in anionic polymerization must possess a vinyl group bonded to one or two electron-withdrawing groups. For instance,...
2.4K
Plastic Behavior01:21

Plastic Behavior

A material's elastic behavior is characterized by the disappearance of stress once the load is removed, allowing the material to return to its original state. However, when stress surpasses the yield point, yielding commences, marking the onset of plastic deformation or permanent set. This change from elastic to plastic behavior is influenced by the peak stress value and the duration before the load is removed. An intriguing observation occurs when a specimen is loaded, unloaded, and...
395
Molecular Weight of Step-Growth Polymers01:08

Molecular Weight of Step-Growth Polymers

Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...
2.6K