Influence of the Welding Process on the Mechanical Characteristics and Fracture of the S700MC High Strength Steel...

This paper focuses on the mechanical properties analysis of the high strength S700MC steel applied in welding joints. The research comprised mechanical tests for checking what the changes of tensile characteristics, mechanical parameters, resistance to impact, and fracture toughness look like in selected regions of the welding joint. Stress-strain curves have shown significant differences in the tensile characteristic shape and the values of Young's modulus, yield stress, ultimate tensile strength, and ductility due to the welding process applied. In the case of Charpy tests, the courses of the accumulated energy, force, deflection, and project velocity are presented, indicating the maximum value of absorbed energy, the same level of force during the first contact of the projectile with the specimens, and the significant variation of the velocity for the impact energy ranging from 50 J up to 300 J. On the basis of the fracture toughness tests, the distributions of the CTOD (Crack Tip Opening Displacement) values are presented for the parent material, HAZ (Heat Affected Zone) and weld. Moreover, the characteristic features of the fatigue pre-crack, transient and crack propagation zones are identified and discussed.