Simple conversion of 3D electrospun nanofibrous cellulose acetate into a mechanically robust nanocomposite...

Cellulose and its derivatives are widely used as nanofibrous biomaterials, but obtaining 3D cellulose nanofibers is difficult and relevant research is scarce. In the present study, we propose a simple method for converting electrospun 3D cellulose acetate/lactic acid nanofibers via calcium hydroxide treatment into a 3D cellulose/calcium lactate nanocomposite matrix. The conversion resulted in producing a stronger nanofibrous matrix (1.382 MPa vs. 0.112 MPa) that is more hydrophilic and cell-friendly compared to the untreated cellulose acetate/lactic acid group. The successful conversion was verified via FTIR, XPS, TGA, DTG, and XRD. The ability of the scaffolds to provide a suitable environment for cell growth and infiltration was verified by CCK assay and confocal microscopy. The porous nature, mechanical strength, and presence of calcium make the 3D cellulose/calcium lactate matrix a promising material for bone tissue engineering.