Bioactive glass versus Arginine dentifrices on the reduction of dentin permeability and acid tolerance
Chantrakorn Champaiboon1,2, Attawood Lertpimonchai1,2, Kullanun Lertpimonchai1
1Department of Periodontology, Faculty of Dentistry, Chulalongkorn University, Bangkok, Thailand.
Objectives:
To compare the efficacy of calcium sodium phosphosilicate (CSPS) and arginine dentifrices on dentin permeability and acid tolerance.
Material And Methods:
Sixty dentin discs were randomly assigned into 3 groups, then brushed for 1 min with CSPS, arginine, or fluoride (control) dentifrices. To test acid tolerance, each disc was soaked in 6% citric acid for 1 min. Dentin permeability was measured before, following brushing, and acid challenge. Ten discs per group were similarly treated and evaluated for tubule occlusion following a single dentifrice application, while other five discs per group were employed in an acid tolerance assay.
Results:
The percentage reduction in dentin permeability was 39.26%, 32.27%, and 21.71% in the arginine, CSPS, and control groups, respectively. The differences in dentin permeability reduction between the arginine and CSPS groups following brushing and acid challenge were not significant (p = 0.398 and p = 0.211, respectively). The arginine dentifrice demonstrated a significant reduction in permeability compared with the control (p = 0.011). In addition, the occlusion exhibited by the arginine and CSPS dentifrices was more resistant to acid challenge compared with that of the control (p < 0.001). From SEM analysis, dentinal tubule occlusion was observed after a single application in all groups. Some open dentinal tubules were detected in the test groups, while almost all of the orifices were open in the fluoride group following acid challenge.
Conclusions:
There is no significant difference between arginine and CSPS dentifrices in reducing dentin permeability following a single application and acid challenge. Following acid challenge, the reduced permeability generated by arginine and CSPS was more stable compared with the fluoride dentifrice.