Bioartificial injectable cartilage implants from demineralized bone matrix/PVA and related studies in rabbit animal...

Functional cartilage tissue engineering needs a substantial, easy to handle scaffold with proper mechanical strength to repair defected area in articular cartilage. In this study, we report the development and characterization of demineralized bone matrix (DBM) in with a poly vinyl alcohol (PVA) to have a proper homogenous injectable scaffold. Injectabiliy of the biodegradable scaffolds, degradation rate, swelling ratio compression and tensile mechanical properties, and viability and proliferation of bone marrow mesenchymal stem cells (BM-MSCs) followed by differentiation of them In-vitro and In-vivo seeded within the scaffold were studied. It demonstrated that the PVA 20% could increase significantly (p < 0.05) the biodegradability of DBM after 720 hours.DBM with 20% of PVA scaffold has significantly higher (p < 0.05) compression and tensile mechanical strength and viscosity. SEM images showed a multilayer of cells on DBM scaffold incorporated with PVA 20%.BM-MSCs on scaffolds, DBM+PVA 20% had a significant growth rate (p < 0.0001) compare to 2D and low concentration of PVA after 21 days of culture. Viability of cells was significantly higher (p < 0.05) on DBM+PVA scaffold compare to DBM. DBM+PVA 20% enhanced cell viability (P < 0.05) compare to DBM scaffold. The PVA presence enhanced chondrogenesis differentiation at the cellular and molecular levels, as evidenced by increased COL II (P < 0.05) and SOX2 upregulation of Chondrogensis-specific genes (p < 0.001). Hyline-like cartilage covered the defect which was confirmed by microscopy and histology assessments. Having considered percentages of PVA with a constant amount of DBM, injectability, compressive mechanical properties, homogeneity of the scaffold, and providing sufficient surface area (12.25 cm²/ml) for cell attachment; 0.35 g/ml of DBM in 20% PVA (w/v) has applicable properties within the ranges of studies which can be proposed for the injectable engineered articular cartilage.