Contribution of Bowman layer to corneal biomechanics

To compare the elastic modulus of thin corneal lamellas using 2D stress-strain extensometry in healthy ex vivo human corneal lamellas with or without the presence of Bowman layer.

Center for Applied Biotechnology and Molecular Medicine, University of Zurich, Switzerland; ELZA Institute, Dietikon, Switzerland; Department of Ophthalmology, Philipps University of Marburg, Germany.

Prospective experimental laboratory study.

Healthy human corneas were stripped of Descemet membrane and the endothelium for Descemet membrane endothelial keratoplasty. After epithelium removal, corneas were divided into 2 groups. In Group 1, Bowman layer was ablated with an excimer laser (20 μm thick, 10 mm). In Group 2, Bowman layer was left intact. Then, a lamella was cut from the anterior cornea with an automated microkeratome. Elastic and viscoelastic material properties were analyzed by 2D stress-strain extensometry between 0.03 and 0.70 N.

Twenty-six human corneas were analyzed. The mean lamella thickness was 160 ± 37 μm in corneas with Bowman layer and 155 ± 22 μm in corneas without. No statistically significant differences between flaps with and without Bowman layer were observed in the tangential elastic modulus between 5% and 20% strain (11.5 ± 2.9 kPa vs 10.8 ± 3.7 kPa, P > .278).

The presence or absence of Bowman layer did not reveal a measurable difference in corneal stiffness. This may indicate that the removal of Bowman layer during photorefractive keratectomy does not represent a disadvantage to corneal biomechanics.