Conductive Polyaniline Doped with Dodecyl Benzene Sulfonic Acid: Synthesis, Characterization, and Antistatic...

A novel method was conducted to synthesize conductive polyaniline (PANI) doped with dodecyl benzene sulfonic acid (DBSA) (PANDB) in xylene by using chemical oxidative polymerization at 25 °C. Meanwhile, the synthesis process was photographed. Results showed as the reaction time was increased, and the color of the product was gradually turned into dark green. The influence of different synthesis time on properties of synthesized PANDB was then examined by a Fourier transform infrared (FTIR) spectrometer, an ultraviolet-visible spectrophotometer (UV-vis), a four-point measurement method, and a Field-emittance scanning electron microscope (FE-SEM). The result indicated that the optimum reaction time was 24 h with conductivity at around 2.03 S/cm. FE-SEM images and the conductivity testing showed that the more needle-like shapes in resulted PANDB, the higher the conductivity. The synthesized PANDB solution was blended with UV curable coating firstly and then coated on polyethylene terephthalate (PET) sheet. The UV coating/PANDB conductive composite films displayed an impressive translucency along with an adequate flexibility at room temperature. The UV coating/PANDB conductive composite film on PET sheet was flexible, transparent, and with antistatic function.