An Analysis of the Casting Polymer Mold Wear Manufactured Using PolyJet Method Based on the Measurement of the...

An important factor having an impact on the condition of machine parts is their surface topography. For instance, in the production of a molded element in casting or injection molding processes, the surface topography of the molding cavity has a significant impact on the surface condition of the product. An analysis of the wear of a mold made with the PolyJet technique was performed in this work, and we examined the surface topography using the stylus method after casting a wax model of the turbine blade. The surface topographies showed a gradual degradation of the mold cavity surface. After the manufacture of 40 castings, there was a significant deformation of the microstructure of the mold cavity. The maximum height value (Sz) parameter had the most dynamic change from 18.980 to 27.920 μm. Its growth dynamics are mainly influenced by maximum peak height (Sp) rather than the maximum pit height (Sv) parameter. In the case of the root mean square height (Sq) and arithmetic mean height (Sa), their gradual increases can be seen from 2.578 to 3.599 μm and from 2.038 to 2.746 μm. In the case of the value of the skewness (Ssk) parameter, a small positive skew was observed. As for the kurtosis (Sku) values, the distributions are clearly leptokurtic.