Microstructure and Properties of As-Cast and Heat-Treated 2017A Aluminium Alloy Obtained from Scrap Recycling

The continuous increase in the consumption of aluminium and its alloys has led to an increase in the amount of aluminium scrap. Due to environmental protection, and to reduce the costs of manufacturing aluminum in recent years, a lot of research is devoted to recycling of aluminum alloys. The paper presents the results of research concerning the possibility of manufacturing standardized alloy 2017A from commercial and post-production scrap by continuous casting. Obtained from recycling process ingots were subjected to analysis of chemical composition and intermetallic phase composition. Based on the results of light microscopy (LM), scanning electron microscopy + electron dispersive spectroscopy (SEM + EDS), and X-ray diffraction (XRD) the following phases in the as-cast state were identified: θ-Al₂Cu, β-Mg₂Si, Al₇Cu₂Fe, Q-Al₄Cu₂Mg₈Si₇, and α-Al₁₅(FeMn)₃(SiCu)₂. During solution heat treatment most of the primary precipitates of intermetallic phases, like θ-Al₂Cu, β-Mg₂Si, and Q-Al₄Cu₂Mg₈Si₇, were dissolved in the solid solution α-Al, and during natural and artificial aging they precipitate as strengthening phases θ-Al₂Cu and Q-Al₄Cu₂Mg₈Si₇ with high dispersion. The highest hardness-150.3 HB-of 2017A alloy was obtained after solution heat treatment from 510 °C and aging at 175 °C. In the static tensile test the mechanical (R_m and R_p0.₂) and plastic (A₅) properties were determined for 2017A alloy in the cast state and after T4 heat treatment. The highest strength properties-tensile strength R_m = 450.5 MPa and yield strength R₀.₂ = 268.7 MPa with good relative elongation A₅ = 14.65%, were obtained after solution heat treatment at 510 °C/6 h/water quenching and natural aging at 25 °C for 70 h. The alloy manufactured from recycled scrap is characterized by relatively high mechanical properties.