Surface Roughness of Cu-Bearing Stainless Steel Affects Its Contact-Killing Efficiency by Mediating the Interfacial...

Numerous studies have found that the surface topography affects the material antibacterial properties by reducing the attachment of bacteria on the surfaces without influencing the viability of the adhered cells. For Cu-bearing alloys with excellent contact-killing properties, bacterial adhesion on the surface is also accompanied by short-range interactions which regulate the toxic effects of the material surface against bacterial cells. Thus, the surface topography of Cu-bearing alloys, as an important factor dominating the exposure level of bacteria on the surfaces, should affect the subsequent contact-killing efficiency. In this work, our major focus was on the regulation mechanism of the surface features on the material-bacterial interactions. We correlated the surface properties including different surface roughnesses of Cu-bearing stainless steel (SS) with the bacterial damage pattern and attempted to clarify the role of surface roughness in mediating the contact-killing behavior of Cu-bearing SS. The results of both atomic force microscopy and scanning electron microscopy investigations showed that E. coli cells experienced the most rapid physical and mechanical damages after incubating with the diamond-polished Cu-bearing SS surface. The bacterial cells noticeably stiffened and the adhesion force significantly increased, as evidenced by force-distance curve measurements. Because of the enhanced hydrophobicity and higher surface potential of the diamond-polished surface, which strengthened the Lewis acid-base attractive forces and weakened the electrostatic barrier between the bacteria and the surface, a higher exposure surface for bacteria was generated. Furthermore, the contact-induced charge transfer, manifested by Cu ion burst release, and reactive oxygen species overexpression contribute to an efficient contact-killing process.