Spectral characterization of hydroxyapatite extracted from Black Sumatra and Fighting cock bone samples: A...

At present, chicken business is occupying a major portion in the market and huge amount of bone wastes are dumped into the open places lead in environmental pollution. In this analysis, natural hydroxyapatite was extracted by thermal calcination process at different temperature ranges from 700 °C, 900 °C and 1100 °C and compared its spectral characteristics. The crystalline nature, functional groups and morphological characteristics of hydroxyapatite obtained from both bone samples were studied using XRD, FTIR and SEM analysis. The crystallite size, lattice parameters, specific surface area, volume and degree of crystallinity were measured using XRD data. The mean grain size of Black Sumatra and Fighting Cock bone hydroxyapatite was 62.67 nm and 31.34 nm respectively. The FTIR spectrum showed major peaks at 634.58 cm^-1 and 470.63 cm^-1, 1413.82 cm^-1 and 1460 cm^-1 indicates the presence of carbonate group and phosphate groups in both samples. The SEM micrograph confirmed the existence of maximum pores in matrix of fighting cock bone than Black Sumatra bone sample. Thus, the comparative analysis concluded that nano-sized hydroxyapetite obtained from bone wastes of fighting cock can be utilized as a low-cost biomaterial for the production of various implant coating materials and substitute for ceramics in bones and dentistry applications.