Syntheses and Characterization of Novel Perovskite-Type LaScO₃-Based Lithium Ionic Conductors

Perovskite-type lithium ionic conductors were explored in the (LiLa_1-)ScO₃ system following their syntheses via a high-pressure solid-state reaction. Phase identification indicated that a solid solution with a perovskite-type structure was formed in the range 0 ≤ x < 0.6. When x = 0.45, (Li_0.45La_0.85)ScO₃ exhibited the highest ionic conductivity and a low activation energy. Increasing the loading of lithium as an ionic diffusion carrier expanded the unit cell volume and contributed to the higher ionic conductivity and lower activation energy. Cations with higher oxidation numbers were introduced into the A/B sites to improve the ionic conductivity. Ce⁴⁺ and Zr⁴⁺ or Nb⁵⁺ dopants partially substituted the A-site (La/Li) and B-site Sc, respectively. Although B-site doping produced a lower ionic conductivity, A-site Ce⁴⁺ doping improved the conductive properties. A perovskite-type single phase was obtained for (Li_0.45La_0.78Ce_0.05)ScO₃ upon Ce⁴⁺ doping, providing a higher ionic conductivity than (Li_0.45La_0.85)ScO₃. Compositional analysis and crystal-structure refinement of (Li_0.45La_0.85)ScO₃ and (Li_0.45La_0.78Ce_0.05)ScO₃ revealed increased lithium contents and expansion of the unit cell upon Ce⁴⁺ co-doping. The highest ionic conductivity of 1.1 × 10^-3 S cm^-1 at 623 K was confirmed for (Li_0.4Ce_0.15La_0.67)ScO₃, which is more than one order of magnitude higher than that of the (LiLa_1-)ScO₃ system.