An improved solvent evaporation method to produce poly (lactic acid) microspheres via foam-transfer

The aim of this work was to study an improved solvent evaporation method to prepare poly (lactic acid) (PLA) microspheres via foam-transfer. Since the foaming process and its transfer were critical to the improved method, they have been studied. Additionally, the delivery capability of foams was studied as a function of the oil/water ratio, the stirring rate, the concentration of polyvinyl alcohol (PVA) and ethanol (EtOH) in the aqueous phase (ω_PVA, ω_EtOH). It was found that foaming varied during the preparation process and it influenced the properties of PLA microspheres. When the oil/water ratio (w/w) ≥ 3:10, stirring rate ≥ 600 r/min, ω_PVA ≥ 1 wt%, and ω_EtOH = 0 wt%, solvent evaporation was able to produce enough foams for foam-transfer, which helped to deliver more than 89 wt% PLA microspheres to the receiving vessel. However, ω_PVA ≤ 0.3 wt% and ω_EtOH = 20 wt% were unfavorable for maintaining the spherical shape of PLA microspheres and caused the aggregation. The methodology was further used to prepare azoxystrobin-loaded PLA microspheres successfully with a high encapsulation efficiency of 86.54%. This work is meaningful since it enables an efficient and continuous route to prepare functional biodegradable polymer microspheres.