Surface Characteristics and Biocompatibility of Ultrafine-Grain Ti after Sandblasting and Acid Etching for Dental
Fan Feng1, Yulu Wu1, Haitao Xin1
1State Key Laboratory of Military Stomatology & National Clinical Research Center for Oral Diseases & Shaanxi Key Laboratory of Stomatology, Department of Prosthodontics, School of Stomatology, The Fourth Military Medical University, Xi'an 710032, China.
Abstract:
This study investigated the surface characteristics and biocompatibility of ultrafine-grain pure titanium (UFG Ti) after sandblasting and acid etching (SLA) treatment to determine an effective method for modification of UFG Ti dental implants. The UFG Ti was processed by equal-channel angular pressing (ECAP). The micromorphology, roughness, and wettability of its surface were studied after SLA modification in different conditions. Rat bone marrow mesenchymal stem cells were subsequently seeded onto the specimens to evaluate the biocompatibility of cell adhesion, proliferation, and differentiation compared with commercially pure titanium (CP Ti). The results showed that surface characteristics of UFG Ti were affected by the pressure of sandblasting and acid etching time in addition to material properties. The favorable hierarchical porous structure that would benefit cell adhesion was formed on the UFG Ti surface when the pressure of sandblasting was 0.6 MPa and the acid etching time was 5 min; at this time, UFG Ti promoted proliferation and differentiation to a greater extent than CP Ti because of its excellent wettability. From this study, it could be seen that UFG Ti can be used as a dental implant material after proper surface modification.