An Improved Mechanical Testing Method to Assess Bone-implant Anchorage
Published on: February 10, 2014
Biomechanical analysis of bioabsorbable suture anchors for rotator cuff repair using osteoporotic and normal bone
Shohei Yamauchi1, Harehiko Tsukada2, Eiji Sasaki1
1Department of Orthopaedic Surgery, Hirosaki University Graduate School of Medicine, 5 Zaifu-cho, Hirosaki, Aomori, 036-8562, Japan.
Background:
This study aimed to compare the failure load of suture anchors used in rotator cuff repair between normal and osteoporotic bone models.
Methods:
A total of 16 anchors made from metal (TwinFix Ti 5.0 or 6.5 mm, Corkscrew FT 4.5, 5.5, or 6.5 mm), polyether ether ketone (HEALICOIL PK [HC-PK] 4.5 or 5.5 mm, SwiveLock PK 4.75 or 5.5 mm), or bioabsorbable material (HEALICOIL RG [HC-RG] 4.75 or 5.5 mm, Corkscrew Bio 4.75, 5.5, or 6.5 mm, SwiveLock BC 4.75 or 5.5 mm) were included. Moreover, 10- and 5-pounds per cubic foot (pcf) Sawbone® models were set as normal and osteoporotic cancellous bone models, respectively. Pullout testing was performed in parallel to the insertion axis at a displacement rate of 12.5 mm/s using a universal testing machine. To evaluate the change in failure load between the two Sawbone® models with different densities, the remaining failure load ratio (RFLR) was defined as the ratio of the failure load in 10 pcf to that in 5 pcf.
Results:
In the 10-pcf Sawbone®, TwinFix Ti 6.5 mm showed the highest mean failure load (304.0 ± 15.2 N). In the 5-pcf Sawbone® model, HC-PK 5.5 mm showed the highest failure load (146.3 ± 5.8 N). Among anchors with the same diameter, HC-PK and HC-RG showed a significantly higher failure load than other anchors in the 10- and 5-pcf Sawbone® models. HC-PK 5.5 mm (62.1%) and HC-PK 4.5 mm (51.1%) have the highest RFLR among anchors with the same diameter.
Conclusions:
HC-PK and HC-RG showed higher failure load than the other anchors in both normal and osteoporotic bone models, except for TwinFix Ti 6.5 mm in the 10-pcf Sawbone® model. Based on our results, bioabsorbable anchors had sufficient failure load for rotator cuff repair in addition to bioabsorbability.