Efficient PbS Quantum Dot Solar Cells with Both Mg-Doped ZnO Window Layer and ZnO Nanocrystal Interface Passivation...

In this paper, a Mg-doped ZnO (MZO) thin film is prepared by a simple solution process under ambient conditions and is used as the window layer for PbS solar cells due to a wide n-type bandgap. Moreover, a thin layer of ZnO nanocrystals (NCs) was deposited on the MZO to reduce carrier recombination at the interface for inverted PbS quantum dot solar cells with the configuration Indium Tin Oxides (ITO)/MZO/ZnO NC (w/o)/PbS/Au. The effect of film thickness and annealing temperature of MZO and ZnO NC on the performance of PbS quantum dot solar cells was investigated in detail. It was found that without the ZnO NC thin layer, the highest power conversion efficiency(PCE) of 5.52% was obtained in the case of a device with an MZO thickness of 50 nm. When a thin layer of ZnO NC was introduced between MZO and PbS quantum dot film, the PCE of the champion device was greatly improved to 7.06% due to the decreased interface recombination. The usage of the MZO buffer layer along with the ZnO NC interface passivation technique is expected to further improve the performance of quantum dot solar cells.