In Situ X-ray Diffraction Investigation of the Crystallisation of Perfluorinated Ce^IV -Based Metal-Organic Frameworks...

We report on the results of an in situ synchrotron powder X-ray diffraction study of the crystallisation in aqueous medium of two recently discovered perfluorinated Ce^IV -based metal-organic frameworks (MOFs), analogues of the already well investigated Zr^IV -based UiO-66 and MIL-140A, namely, F4_UiO-66(Ce) and F4_MIL-140A(Ce). The two MOFs were originally obtained in pure form in similar conditions, using ammonium cerium nitrate and tetrafluoroterephthalic acid as reagents, and small variations of the reaction parameters were found to yield mixed phases. Here, we investigate the crystallisation of these compounds, varying parameters such as temperature, amount of the protonation modulator nitric acid and amount of the coordination modulator acetic acid. When only HNO₃ is present in the reaction environment, only F4_MIL-140A(Ce) is obtained. Heating preferentially accelerates nucleation, which becomes rate determining below 57 °C. Upon addition of AcOH to the system, alongside HNO₃ , mixed-phased products are obtained. F4_UiO-66(Ce) is always formed faster, and no interconversion between the two phases occurs. In the case of F4_UiO-66(Ce), crystal growth is always the rate-determining step. A higher amount of HNO₃ favours the formation of F4_MIL-140A(Ce), whereas increasing the amount of AcOH favours the formation of F4_UiO-66(Ce). Based on the in situ results, a new optimised route to achieving a pure, high-quality F4_MIL-140A(Ce) phase in mild conditions (60 °C, 1 h) is also identified.