Blue TiO₂ nanotube arrays as semimetallic materials with enhanced photoelectrochemical activity towards water...

In the past years there has been a great interest in self-doped TiO₂ nanotubes (blue TiO₂ nanotubes) compared to undoped ones owing to their high carrier density and conductivity. In this study, blue TiO₂ nanotubes are investigated as photoanode materials for photoelectrochemical water splitting. Blue TiO₂ nanotubes were fabricated with enhanced photoresponse behavior through electrochemical cathodic polarization on undoped and annealed TiO₂ nanotubes. The annealing temperature of undoped TiO₂ nanotubes was tuned before cathodic polarization, revealing that annealing at 500 °C improved the photoresponse of the nanotubes significantly. Further optimization of the blue TiO₂ nanotubes was achieved by adjusting the cathodic polarization parameters. Blue TiO₂ nanotubes obtained at the potential of -1.4 V (vs. SCE) with a duration of 10 min exhibited twice more photocurrent response (0.39 mA cm^-2) compared to the undoped TiO₂ nanotube arrays (0.19 mA cm^-2). Oxygen vacancies formed through the cathodic polarization decreased charge recombination and enhanced charge transfer rate; therefore, a high photoelectrochemical activity under visible light irradiation could be achieved.