Omnidirectional and Broadband Antireflection Effect with Tapered Silicon Nanostructures Fabricated with Low-Cost and...

In this report, we present a process for the fabrication and tapering of a silicon (Si) nanopillar (NP) array on a large Si surface area wafer (2-inch diameter) to provide enhanced light harvesting for Si solar cell application. From our N,N-dimethyl-formamide (DMF) solvent-controlled spin-coating method, silica nanosphere (SNS in 310 nm diameter) coating on the Si surface was demonstrated successfully with improved monolayer coverage (>95%) and uniformity. After combining this method with a reactive ion etching (RIE) technique, a high-density Si NP array was produced, and we revealed that controlled tapering of Si NPs could be achieved after introducing a two-step RIE process using (1) CHF₃/Ar gases for SNS selective etching over Si and (2) Cl₂ gas for Si vertical etching. From our experimental and computational study, we show that an effectively tapered Si NP (i.e., an Si nanotip (NT)) structure could offer a highly effective omnidirectional and broadband antireflection effect for high-efficiency Si solar cell application.