Suppressed Degradation and Enhanced Performance of CsPbI₃ Perovskite Quantum Dot Solar Cells via Engineering of...

CsPbI₃ perovskite quantum dots (CsPbI₃-PQDs) have recently come into focus as a light-harvesting material that can act as a platform through which to combine the material advantages of both perovskites and QDs. However, the low cubic-phase stability of CsPbI₃-PQDs in ambient conditions has been recognized as a factor that inhibits device stability. TiO₂ nanoparticles are the most regularly used materials as an electron transport layer (ETL) in CsPbI₃-PQD photovoltaics; however, we found that TiO₂ can facilitate the cubic-phase degradation of CsPbI₃-PQDs due to its vigorous photocatalytic activity. To address these issues, we have developed chloride-passivated SnO₂ QDs (Cl@SnO₂ QDs), which have low photocatalytic activity and few surface traps, to suppress the cubic-phase degradation of CsPbI₃-PQDs. Given these advantages, the CsPbI₃-PQD solar cells based on Cl@SnO₂ ETLs show significantly improved device operational stability (under conditions of 50% relative humidity and 1-sun illumination), compared to those based on TiO₂ ETLs. In addition, the Cl@SnO₂-based devices showed improved open circuit voltage and photocurrent density, resulting in enhanced power conversion efficiency (PCE) up to 14.5% compared to that of TiO₂-based control devices (PCE of 13.8%).