One-pot fabrication of lignin-based aromatic porous polymers for efficient removal of bisphenol AF from water

To remove the bisphenol AF (BPAF) from aqueous solution, two different types of lignin-based aromatic porous polymers (LAPP-1 and LAPP-2) were fabricated via one-pot crosslinking of lignin with 1,4-dichloroxylene and 4,4'-bis(chloromethyl)-1,1'-biphenyl, respectively. The successful synthesis of LAPPs was confirmed by FTIR and XPS, SEM, TEM and N₂ adsorption-desorption analysis. Then, batch adsorption experiments were conducted to investigate adsorption properties toward BPAF. Based on the results, the adsorption processes were in accordance with the pseudo-second-order kinetic model and the Freundlich isotherm model, and the thermodynamic studies showed that the adsorption was a spontaneous and exothermic process. It is remarkable that LAPPs exhibited good adsorption performance in wide ranges of pH and ionic strength as well as in recycling process. Notably, compared to LAPP-1, LAPP-2 exhibited higher adsorption capacity for BPAF, which can be ascribed to its higher porosity and content of aromatic ring. Moreover, the comprehensive analysis of experimental and theoretical results indicated that the π-π interactions and pore adsorption may jointly drive the uptake process of BPAF. Considering the simple fabrication method employed and excellent BPAF adsorption performance, LAPPs provided new insights into the development of advanced lignin-based adsorbents for removal of BPAF from water.