Removal of diclofenac from aqueous solutions by adsorption on thermo-plasma expanded graphite

The adsorption of diclofenac on thermo-plasma expanded graphite (a commercial product) from water solutions was investigated. The adsorbent material was characterized by SEM, TEM, BET, Raman and X-ray diffraction analyses. Typical diffractogram and Raman spectrum of graphitic material, dimension of 24.02 nm as crystallite dimension and a surface area of 47 m² g^-1 were obtained. The effect of pH on the adsorption capacity was evaluated in the range 1-7 and the adsorption mechanism was described by kinetic and isothermal studies. Pseudo-second order and Dubinin-Radushkevich models agreed with theoretical values of adsorption capacity (i.e. 400 and 433 mg g^-1, respectively) and resulted to be the best fit for kinetics and isothermal experimental data. The thermodynamics of the process was evaluated by plotting the adsorption capacity/concentration ratio at the equilibrium as a function of different values of the multiplicative inverse of temperature. Moreover, the adsorbent regeneration was also investigated, comparing two different remediation techniques. Solvent washing performed with NaOH 0.2 M and thermo-treatment carried out by heating in an oven at 105 °C for 2 h and then at 200 °C for 4 h. The thermo-treatment was the best technique to regenerate the adsorbent, ensuring same performance after 4 cycles of use and regeneration.