Evaluation of a new cemented highly cross-linked all-polyethylene cup: a prospective and randomised study assessing
Volker Otten1, Daniel Wästerlund1, John Lindbjörn1
1Department of Surgical and Perioperative Sciences, Orthopaedics, Umeå University, Umeå, Sweden.
Background And Purpose:
The aim of this prospective, randomised and controlled study was to evaluate the wear and fixation properties of a new cemented highly cross-linked all-polyethylene (HXLPE) cup in comparison with a conventional cemented ultra-high molecular weight polyethylene (ConvPE) cup using radiostereometric analysis (RSA).
Patients And Methods:
A total of 58 patients (58 hips) with primary osteoarthritis (OA) were enrolled in a randomised controlled trial to receive either a ConvPE cup (control) or HXLPE cup (intervention) with identical geometry. The subjects were randomised in a 1:1 ratio. The primary endpoint was proximal wear measured as femoral head penetration into the cup, secondary outcomes were 3D-wear and annual proximal wear from 1 to 5 years. Cup fixation was measured as movement of the cup in relation to the acetabular bone with proximal migration being the primary outcome measure, 3D-migration and change in inclination as secondary outcomes. The patients were followed for 5 years with RSA performed postoperatively, at 3, 12, 24, and 60 months.
Results:
The HXLPE displayed a lower median proximal femoral head penetration compared to ConvPE, with a median difference at 2 years of -0.07 mm (95% CI, -0.10 to -0.04 mm), and -0.19 mm (95% CI, -0.27 to -0.15 mm) at 5 years. Annual proximal wear between 1 and 5 years was 0.03 mm/year for HXLPE and 0.06 mm/year for ConvPE (mean difference 0.05 mm, [95% CI, 0.03-0.07 mm]). Proximal migration, 3D migration and change in inclination was numerically slightly higher for HXLPE, albeit not statistically significant.
Conclusions:
Compared to ConvPE, the HXLPE cup displayed significantly lower polyethylene wear. Cup migration was not statistically significant different.
Clinicaltrials.Gov Identifier:
NCT04322799.