Synthesis and characterization of metal-organic framework/biomass-derived CoSe/C@C hierarchical structures with...

Metal selenide has attracted much attention for use in rechargeable batteries due to its excellent conductivity and considerable capacity. However, it is still necessary to achieve a long cycle life and excellent Na+ storage performance to enable its practical application. Volume expansion and poor stability of selenide during operation also hinder its industrial applications. As metal-organic frameworks and aerogels possess porous structures, carbon materials derived from them can effectively reduce the volume expansion of selenide, resulting in improving cycling stability and enhancing Na+ storage. In this work, CoSe/C@C composites with a hierarchical structure were successfully prepared by freeze-drying and in situ selenization as anode materials. The CoSe/C@C composites exhibited superior cycling stability (a capacity of 332.3 mA h g-1) and capacity retention (63.1% compared to the second cycle) at 200 mA g-1, after 500 cycles. CoSe/C@C also exhibited a high rate performance of 403.4 mA h g-1 at 2 A g-1. Moreover, thanks to the high capacitance contribution and some redox reactions during cycling, the CoSe/C@C electrode possesses outstanding rate capability.