Microroughness induced biomimetic coating for biodegradation control of magnesium

Herein we explore a combination of anodization induced micro-roughness and biomimetic coating on pure magnesium (Mg) metal at different applied voltages to control adhesion, biodegradation, and corrosion performance in simulated body fluid solution. The anodic film was fabricated using two different potentials, 3 and 5 V, respectively, to create microroughness on the Mg surface. The microroughened Mg surface was subsequently coated with a biomimetic silk thin film; and the characteristics of the treated Mg-substrates were evaluated using various spectroscopic, microscopic, immersion, and electrochemical techniques. A number of independent measurements, including hydrogen evolution, weight loss and electrochemical methods were employed to assess the corrosion characteristics. The silk-coated anodized samples revealed dramatically reduced degradation rate in terms of volume of hydrogen gas generation and weight loss compared to the respective anodized but uncoated, which revealed that optimized biomimetic silk-coated Mg surface (anodized at 5 V and subsequently biomimetic silk-coated ANMg_5V) exhibited the best corrosion performance among all other tested samples. The ANMg_5V Silk showed the highest polarization resistance (46.12 kΩ·cm²), protection efficiency (>0.99) and lowest corrosion rate (only 0.017 mm/year) relative to untreated Mg (8.457 mm/year), and anodized Mg (1.039 for anodized at 3 V and 0.986 for anodized at 5 V) surface due to the formation of a pore-free dense biomimetic protective film over Mg surface. The results of the cytotoxicity test confirm that silk-coated samples are significantly less cytotoxic compared to bare and anodized Mg samples. With enhanced corrosion resistance and cytocompatibility, silk-coated Mg could be a potential material for clinical applications.