Effects of Polyvinyl Alcohol on Drug Release from Nanocomposite Particles Using Poly (L-lactide-co-glycolide)

The effects of polyvinyl alcohol (PVA) on the release behavior of polymer nanoparticles from nanocomposite particles using amino acids were investigated. Rifaximin (RFX) was used as a hydrophobic drug model. RFX-loaded poly(L-lactide-co-glycolide) (PLLGA) nanoparticles were prepared using an antisolvent diffusion method. They were then spray-dried with equal amounts of amino acids to prepare the nanocomposite particles. The mean diameters of nanocomposite particles were 2.86-5.42 μm. The particle size increased as the concentration of PVA aqueous solution increased. The mean diameters of RFX-loaded PLLGA nanoparticles were 150-160 nm; however, the particle size distributions of those prepared using 0.25% (w/v) PVA aqueous solution differed significantly immediately after preparation and after redispersion from nanocomposite particles. The release test results of nanocomposite particles revealed that those prepared using 0.25% and 0.50% (w/v) aqueous PVA solutions rapidly released RFX. In contrast, particles prepared using 2.00 and 4.00% (w/v) PVA aqueous solution showed sustained drug release. The results of drug release tests of nanoparticles redispersed from nanocomposite particles showed that the nanoparticles prepared using 0.50% and 2.00% (w/v) PVA aqueous solution suppressed the initial burst. Therefore, we considered that the results of the drug release behavior of the nanoparticles in these particles reflectsreflect the release behavior of the nanoparticles from the nanocomposite particles. These results indicate that the rate of redispersion from nanocomposite particles to nanoparticles can be controlled by changing the concentration of PVA aqueous solution.