Synthesis and Characterization of Various Doped TiO₂ Nanocrystals for Dye-Sensitized Solar Cells

Few works are reported on solvothermal preparation of nanoparticles by utilizing acetone alone without a surfactant. This synthesis approach is found to be prominent for producing the mesoporous structure, which is crucial in improving the dye loading of the photoanode. In addition, doping of metal ions is advantageous in order to bring down the excitation energy, which is promising for boosting the performance of the doped oxides. This research aims to synthesize various kinds of doped-TiO₂ nanocrystals to serve as photoanode materials in dye-sensitized solar cells (DSSCs). An X-ray diffraction study evidenced the existence of the crystalline phase in pure and doped-TiO₂ nanocrystals. Rietveld refinement study showed the mixed phases of crystalline TiO₂ in the CrT, CuNT, and ST as compared to a single anatase phase in the samples PT, AgT, BT, CoT, FeT, SnT, ZT, VT, and ZMT. The absorption spectroscopy analysis demonstrated the reduced optical band gap from 3.10 to 2.79 eV. Scanning electron microscopy investigation endorsed the formation of TiO₂ mesoporous microspheres with a mean diameter ranging from 200 to 331 nm along with a nanocrystal diameter ranging from 10 to 20 nm. Doping with the different dopants enhanced the conversion efficiency of DSSCs from 1.31 to ∼6%. Furthermore, we have performed the electrochemical impedance spectroscopy of DSSCs, and the findings are presented.