Complex Resonant Scattering Behavior in the Surface Plasmon Resonance Imaging Microscopy of Single Gold Nanorods

Diffraction patterns observed in surface plasmon resonance imaging (SPRI) microscopy measurements of single gold nanorods (AuNRs) exhibit a complex behavior at wavelengths near the longitudinal plasmonic resonance band. SPRI microscopy measurements at 814 nm from AuNRs in three samples with resonance extinction maxima at 670, 816, and 980 nm reveal a variety of diffraction patterns with central peaks that are either positive, negative, or biphasic. A unitless ratio parameter M_R (-1 ≤ M_R ≤ 1) is created to describe the distribution of diffraction patterns. A purely negative (M_R = -1) central peak is observed for 30%, 57%, and 98% of the diffraction patterns in the 670, 816, and 980 nm samples, respectively. These results along with a theoretical modeling of the diffraction patterns with an anisotropic complex scattering coefficient suggests that this behavior only occurs for AuNRs when the laser wavelength used in SPRI experiments is shorter than the AuNR plasmonic resonance maxima, that is, in the anomalous dispersion region.