Comparison of Wear Resistance of Prefabricated Composite Veneers Versus Ceramic and Enamel

To measure surface roughness before and after wear-tests of two different prefabricated composite veneers and compare them to ceramic veneers and human dental enamel.

Roughness (Ra-values) of two prefabricated composite veneers (Visalys Veneer Chairside (VIS) and Componeer (COM)) were compared to lithium disilicate Veneers (e.max CAD) and dental enamel (DENT) in vitro. In total n = 45 specimens per material and enamel samples were used for wear-tests. Wear-out tests were conducted by abrasion tests with a toothbrush simulator (22,000 strokes/ 100 g load; approximately equal to two years of cleansing) and erosion tests were carried out using citric acid (pH 1.57). Ra- and Sa-values were detected by white light interferometer before and after wear-tests. Data were analyzed with ANOVA followed by Games-Howell post hoc test and t-test (α = 0.05).

At baseline the lowest Ra- and Sa-values were found in VIS (Ra: 0.01 µm; Sa: 0.04 µm) while DENT revealed significantly higher surface roughness (Ra: 0.11 µm, p < 0.05; Sa: 0.30, p = 0.186). COM had significantly higher Ra-values (Ra: 0.10 µm; Sa: 0.22 µm) after abrasion, while e.max CAD was most resistant to the treatments (Ra: 0.01 µm, p < 0.05; Sa: 0.05 µm, p < 0.05). Compared to DENT all veneers were significantly less affected by citric acid (p < 0.001).

Prefabricated composite veneers have demonstrated less wear after abrasion and erosion tests compared to DENT, nevertheless, they revealed more wear compared to e.max CAD.