Reconstruction of critical-size segmental defects in rat femurs using carbonate apatite honeycomb scaffolds

Critical-size segmental defects are formidable challenges in orthopedic surgery. Various scaffolds have been developed to facilitate bone reconstruction within such defects. Many previously studied scaffolds achieved effective outcomes with a combination of high cost, high-risk growth factors or stem cells. Herein, we developed honeycomb scaffolds (HCSs) comprising carbonate apatite (CO₃ Ap) containing 8% carbonate, identical to human bone composition. The CO₃ Ap HCSs were white-columned blocks harboring regularly arranged macropore channels of a size and wall thickness of 156 ± 5 μm and 102 ± 10 μm, respectively. The compressive strengths of the HCSs parallel and perpendicular to the macropore channel direction were 51.0 ± 11.8 and 15.6 ± 2.2 MPa, respectively. The HCSs were grafted into critical-sized segmental defects in rat femurs. The HCSs bore high-load stresses without any observed breakage. Two-weeks post-implantation, calluses formed around the HCSs and immature bone formed in the HCS interior. The calluses and immature bone matured until 8 weeks via endochondral ossification. At 12 weeks post-implantation, large parts of the HCSs were gradually replaced by newly formed bone. The bone reconstruction efficacy of the CO₃ Ap HCSs alone was comparable to that of protein and cell scaffolds, while achieving a lower cost and increased safety.