In-vitro glistening formation in six different foldable hydrophobic intraocular lenses
Tamer Tandogan1, Gerd U Auffarth2, Hyeck-Soo Son1
1The David J. Apple International Laboratory for Ocular Pathology and International Vision Correction Research Centre (IVCRC), Department of Ophthalmology, University of Heidelberg, INF 400, 69120, Heidelberg, Germany.
Background:
Glistenings describe small, refractile microvacuoles that may arise within the intraocular lens (IOL) material and reduce the patients' quality of vision. Lenses composed of hydrophobic acrylic material are particularly affected by glistening formation. In this study, we compared the tendency of glistening formation in six different types of hydrophobic acrylic intraocular lenses (IOLs).
Methods:
We used a well-established accelerated laboratory method to develop glistenings in the following IOLs: Vivinex XY1 (Hoya), AcrySof SN60WF (Alcon), Tecnis ZCB00 (AMO), Avansee PN6A (Kowa), Aktis SP NS-60YG (Nidek), and CT Lucia 601P (Zeiss). IOLs were first immersed in saline at 45 °C for 24 h and then at 37 °C for 2.5 h in a water bath. Microvacuole (MV) density and size (Miyata grading) were documented and calculated using an image analysis program.
Results:
The mean glistening density [MV/mm2] and mean Miyata grading (in brackets) were: Vivinex: 11.6 ± 5.7 (0), SN60WF: 264.4 ± 110.3 (2.6), Tecnis: 6.0 ± 2.8 (0), Avansee: 2.2 ± 0.7 (0), Aktis: 851.4 ± 59.4 (3+) and CT Lucia: 71.0 ± 71.6 (1).
Conclusions:
While all tested IOLs showed glistenings with the accelerated laboratory method, the Aktis and SN60WF showed the highest microvacuole density, followed by the CT Lucia. In comparison, the Vivinex, Tecnis, and Avansee IOLs showed far fewer number of glistenings.