Preparation and pore-forming mechanism of hydrogen bond and ionic bond double-driven chitosan-based mesoporous carbon

Using chitosan as the carbon source, F127 as the template, and sodium tripolyphosphate as cross-linking agent, a hydrogen bond and ionic bond double-driven mesoporous carbon material was prepared via the sol-hydrothermal method and its formation mechanism was discussed. According to the results from FTIR, Raman, XPS, physical adsorption analyzer, SEM, TEM, and TG-IR, the mesoporous carbon material was formed under the synergistic effect of hydrogen bond and ionic bond has a mesoporous volume of 0.44 cm³/g, a BET surface area of 262 m²/g, and possesses the ideal unimodal distribution around 2.20 nm. The mesopores are originated from the degradation of hydrophobic segment PPO of F127, and the micropores come from the gases CO₂, CO, NH₃, CH₄, tetraethylene glycol dimethyl ether, and 2,6-diisopropylphenyl isocyanate produced during the degradation of prepolymers. The maximum adsorption capacity of this mesoporous carbon for tannic acid (Sips model) at 30 °C is 70.4 mg/g.