Analyzing growth kinematics and fractal dimensions of molybdenum disulfide films

Though the positive role of alkali halides in realizing large area growth of transition metal dichalcogenide layers has been validated, the film-growth kinematics has not yet been fully established. This work presents a systematic analysis of the MoS₂morphology for films grown under various pre-treatment conditions of the substrate with sodium chloride (NaCl). At an optimum NaCl concentration, the domain size of the monolayer increased by almost two orders of magnitude compared to alkali-free growth of MoS₂. The results show an inverse relationship between fractal dimension and areal coverage of the substrate with monolayers and multi-layers, respectively. Using the Fact-Sage software, the role of NaCl in determining the partial pressures of Mo- and S-based compounds in gaseous phase at the growth temperature is elucidated. The presence of alkali salts is shown to affect the domain size and film morphology by affecting the Mo and S partial pressures. Compared to alkali-free synthesis under the same growth conditions, MoS₂film growth assisted by NaCl results in ≈81% of the substrate covered by monolayers. Under ideal growth conditions, at an optimum NaCl concentration, nucleation was suppressed, and domains enlarged, resulting in large area growth of MoS₂monolayers. No evidence of alkali or halogen atoms were found in the composition analysis of the films. On the basis of Raman spectroscopy and photoluminescence measurements, the MoS₂films were found to be of good crystalline quality.