Effects of cyclic loading on the mechanical properties and failure of human patellar tendon

Patellar tendinopathy is a common overuse injury in sports such as volleyball, basketball, and long-distance running. Microdamage accumulation, in response to repetitive loading of the tendon, plays an important role in the pathophysiology of patellar tendinopathy. This damage presents mechanically as a reduction in Young's modulus and an increase in residual strain. In this study, 19 human patellar tendon samples underwent cyclic testing in load control until failure, segmented by four ramped tests where digital image correlation (DIC) was used to assess anterior surface strain distributions. Ramped tests were performed prior to cyclic testing and at timepoints corresponding to 10%, 20%, and 30% of cyclic stiffness reduction. Young's modulus significantly decreased and cyclic energy dissipation significantly increased over the course of cyclic testing. The DIC analysis illustrated a heterogeneous strain distribution, with strain concentrations increasing in magnitude and size over the course of cyclic testing. Peak stress and initial peak strain magnitudes significantly correlated with the number of cycles to failure (r² = 0.65 and r² = 0.57, respectively, p < 0.001); however, the rates of peak cyclic strain and modulus loss displayed the highest correlations with the number of cycles to failure (r² = 96% and r² = 86%, respectively, p < 0.001). The high correlation between the rates of peak cyclic strain and modulus loss suggest that non-invasive methods to continuously monitor tendon strain may provide meaningful predictions of overuse injury in the patellar tendon.