The microstructure and property of Al-Si alloy improved by the Sc-microalloying and Y2O3 nano-particles
Jiqiang Chen1,2, Feng Wen1, Chao Liu1
1Faculty of Materials, Metallurgy and Chemistry, Jiangxi University of Science and Technology, Ganzhou, China.
Abstract:
The effect of Sc-microalloying and Y2O3 nano-particles on the microstructure and mechanical properties of as-cast Al-5.5Si alloy is studied by means of optical microscopy, transmission electron microscopy, hardness test and tensile test. The influence of annealing treatment on the microstructure and properties of the Al-Si alloys is also investigated as well. The results show that the addition of Sc and Y2O3 nano-particles could significantly improve the mechanical property of the Al-Si alloy. The ultimate tensile strength and yield strength of Al-Si-Sc/Y2O3 alloy are improved by around 45 and 71%, respectively, when compared to that of the Al-Si alloy. The effect of the nanosized particles (precipitated and added) on strengthening and deformation of Al-Si alloy is analyzed and discussed in detail. The results of annealing treatment indicate that the change in mechanical property of the Al-Si-Sc alloy during annealing treatment is mainly associated with the precipitation of the secondary Si phase.