Effective adsorption of bisphenol A from aqueous solution over a novel mesoporous carbonized material based on spent...

In this study, the novel mesoporous carbonized material (HSBE/C) was prepared from clay/carbon composite (SBE/C) treated with hydrofluoric acid (HF) for the first time, and was employed to efficiently adsorb bisphenol A (BPA) in water. Specifically, SBE/C was derived from the pyrolysis of spent bleaching earth (SBE), an industrial waste. HF removed SiO₂ from SBE/C and increased the specific surface area of HSBE/C (from 100.21 to 183.56 m²/g), greatly providing more adsorption sites for enhanced BPA adsorption capacity. The Langmuir monolayer maximum adsorption capacity of HSBE/C (103.32 mg/g) was much higher than the commercial activated carbon (AC) (42.53 mg/g). The adsorption process by HSBE/C followed well with the Freundlich isotherm model and the pseudo-second-order kinetic model and also was endothermic (ΔH⁰ > 0) and spontaneous (ΔG⁰ < 0). Based on the systematic characterization and factor experiment (temperature, dosage, initial pH, co-existing ions), BPA adsorption mechanism by HSBE/C likely included the hydrogen bonding, electrostatic interaction, and hydrophobic interaction. Moreover, there was no secondary pollution during the total adsorption process. Extraordinary, HSBE/C manifested stability by NaOH desorption regeneration. This study provides a new sight for application of waste-based materials as the promising adsorbents in the treatment of endocrine disruptors.