Fibrous scaffolds of Ag/Fe co-doped hydroxyapatite encapsulated into polycaprolactone: Morphology, mechanical and in...

The development of a scaffold matrix to promote wound healing is a critical requirement to improve the health care system. For this purpose, electrospun scaffolds of polycaprolactone (PCL) have been encapsulated with hydroxyapatite (HAP) doped with different contributions Ag ions. The obtained scaffolds have been investigated by XRD, FTIR and FESEM. It was shown that scaffolds were configured as cross-linked network with diameters around 0.6, 0.9, 2.1, and 2.5 μm for 0.0Ag/Fe-HAP@PCL, 0.4Ag/Fe-HAP@PCL, 0.6Ag/Fe-HAP@PCL, and 0.8Ag/Fe-HAP@PCL, respectively. Additionally, the composition of 0.8Ag/Fe-HAP@PCL exhibited the highest roughness average of 34 nm, while the inorganic root of co-dopant HAP recorded 44.8 nm. The mechanical properties have been investigated and showed that the maximum strain at break was about 129.31 ± 5.4% at no additional Ag ions, and reached its lowest value of 103.02 ± 3.5% at 0.2Ag/Fe-HAP@PCL. On the other hand, cell viability increased from 94.74 ± 4 to 98.9 ± 4% for 0.0Ag/Fe-HAP@PCL and 0.6Ag/Fe-HAP@PCL, respectively. Further, the antibacterial activity was investigated and exhibited that the inhibition zones of E. coli increased from 0.0 at 0.0Ag/Fe-HAP@PCL to 7.5 ± 1.3 mm for 0.8Ag/Fe-HAP@PCL. Moreover, the in vitro cell attachment showed that fibroblast cells proliferated and spread on the fibers' surface and through scaffolds' porosity.